ADHESIVE FOR ELECTRIC/ELECTRONIC COMPONENTS
FB500Z B/W
FB500Z is one-component room temperature curing elastic adhesive based on silane terminated
polymers and free from organotin compounds. FB500Z is suitable for adhesion and seal of
electric/electronic components and the other uses in which the use of tin compounds is restricted.
' For uses restricted the use of tin compounds.
' For bonding metals or rigid plastics.
' For bonding between adherends with different thermal expansion confficients.
' For uses required resistant to impact or vibrations.
* FB500Z is not applicable to polyethylene, polypropylene, silicone resin, and fluorine resin.
' Meets the requirements specified in Annex XVII of REACH, Commission Regulation (EU)
No. 276/2010.
' Free from 6 RoHS restricted substances (cadmium, lead, mercury, hexavalent chromium, and its
compounds, and specific brominated flame retardants (PBBs and PBDEs)).
' Free from low molecular cyclic polysiloxanes that can cause contact failure.
' Resistance to stress or thermal change because of elasticity after curing.
' Flame retardant equivalent to UL94 V-0 (File No. E325882)
' CTI equivalent to UL746A PLC:0 (File No. E325882)
' HWI equivalent to UL746A PLC:0 (File No. E325882)
' HAI equivalent to UL746A PLC:0 (File No. E325882)
Features
Uses
2 / 4
Item Test method Properties
Appearance Visual observation —
FB500ZBBlack paste
FB500ZWWhite paste
Viscosity [10rpm] JIS K 6833-1 23°C 50150 Pas
Film formation time Surface touching 23°C, 50%RH 515 min.
Specific gravity JIS K 6833-1 23°C 1.57±0.05
Flash point
Closed-cup
flash point test
69°C
This table shows typical values, which are not guaranteed.
The following data were measured under standard conditions of 23±2°C and 50±5%RH unless
otherwise stated.
1. Properties after curing
Tests Conditions Properties
Physical properties
JIS K 6251 No.3 dumbbell
Thickness : 2mm
Cross-head speed : 200 mm/min
50% modulus N/mm2 3.9
Maximum tensile stress N/mm2 3.9
Elongation at break % 50
Durometer hardness 23°C 50%RH Type A 85
Volume resistivity
DC 500V
20℃60RH
Ωcm 1.1×1012
Technical data
Properties
3 / 4
2. Tensile shear strength (according to JIS K 6850))
Lap area25 mm×12.5 mm
Adhesive thickness0.2 mm
Cross-head speed5 mm/ min.
Aging conditions23℃50%RH×7d (plastic), 23℃50%RH×14d (metal)
adherends kind of material Thickness surface preparation
adhesive strength
[N/mm2]
PMMA - 3 mm Degreased with methanol 2.28
PC - 3 mm Degreased with methanol 1.97
ABS - 3 mm Degreased with methanol 2.05
PCABS - 3 mm Degreased with methanol 2.07
PBT - 3 mm Degreased with methanol 1.50
Stainless steel SUS304 1.5 mm Degreased with acetone 2.85
Aluminium JIS A 1050P 2 mm Degreased with acetone 2.82
4 / 4
120 ml laminate tube container 20/cace
(4 strapped boxes each containing 5 single product boxes)
333 ml paper tube container 20/case
(2 strapped boxes each containing 10 single product boxes)
Color FB500ZB = black, FB500ZW = white
This technical information is based on the tests and studies carried out by Konishi Co., Ltd., and we
believe it is reliable. However, the properties and characteristics may change depending on conditions,
for example temperature, humidity, adherends, thickness of the adhesive layer, and usage environment.
The use conditions should be determined by user’s tests.
Package volume

RELATED PRODUCTS
 
X

Convenient
Competitive Quotes
Choice of Suppliers
 
sending enquiry ....

unable to instantiate your call right now. please try after some time.

close

©Copyright HelloTrade.com